| Density |
ISO 11 83 |
g/cm3 |
1.78 |
| Water absorption (24h at 23°C) |
ISO 62 (method 1) |
% |
<0.04 |
| Melt Flow Index |
ASTM D 1238 |
|
|
| 230°C, 10 kg |
g/10 min |
- |
| 230°C, 5 kg |
g/10 min |
24 |
| 230°C, 2.16 kg |
g/10 min |
8 |
| Tensile |
ASTM D368 |
|
|
| Tensile stress at yield |
|
MPa/psi |
53-57/7685-8265 |
| Tensile stress at break |
23°C, 50mm/min |
MPa/psi |
35-50/5075-7250 |
| Elongation at yield |
|
% |
5-10 |
| Elongation at break |
|
% |
20-50 |
| Modulus |
23°C, 1mm/min |
MPa/psi |
2500/362500 |
| Flexion |
ASTM D256 |
|
|
| Maximum load |
23°C |
MPa/psi |
78/11310 |
| Modulus |
2mm/min |
MPa/psi |
2200/319000 |
| Izod impact (notched V 10mm at 23°C -4mm thick |
ASTM D256 |
J/m |
65 |
| Shore D Harness (2mm thick) |
ASTM D2240 |
- |
77 |
| Abrasion resistance |
TABER CS 10/1 kg |
mg/1000 rev |
5-10 |
| Friction Coefficient : Static |
ASTM D 1894 |
- |
0.2-0.4 |
| Friction Coefficient : Dynamic |
|
- |
0.2-0.3 |
| Crystallinity by DSC |
ASTM D3418 |
|
|
| Melting point |
|
°C/°F |
174/345 |
| Heat of fusion (80°C to end of melting) |
|
J/g |
62 |
| Crystallizing point |
|
°C/°F |
139/282 |
| Crystallizing heat |
ASTM D368 |
J/g |
58 |
| VICAT point (4mm thick) |
ISO 306 |
|
|
| Load 1kg |
23°C, 50mm/min |
°C/°F |
170/338 |
| Deflection temperature (4mm thick) |
ASTM D648 |
|
|
| Load 0.46 MPa |
after annealing |
°C/°F |
147/294 |
| Load 1.82 MPa |
23°C, 1mm/min |
°C/°F |
112/234 |
| Glass transition (Tg) |
DMTA |
°C/°F |
-32/-26 |
| Brittleness temp (on 2mm pressed sheet) |
ASTM D746 A |
°C/°F |
0-10/32-50 |
| Molding shrinkage |
|
% |
2-3 |
| Thermal stability |
TGA beginning & at 1% |
°C/°F |
375-400/707-752 |
| Linear thermal expansion coefficient |
weight loss in air |
10-6k1 |
120-140 |
| Thermal conductance at 23°C |
ASTM D696 |
W/m.k |
0.2 |
| Specific heat |
ASTM C 177
23°C & 100°C |
J/g.k |
1.2-1.6 |
| Surface resistivity |
ASTM D 257 |
|
|
| Voltage < 1V. after 2min-500Vat 23°C |
DIN 53483 |
|
|
| Volume resistivity |
ASTM D 257 |
ohm/square |
>1.10 11 |
| Intensity = 10mA, after 2min at 23°C |
DIN 53483 |
ohm/cm |
>1.10 14 |
| UL-94 Flammability test |
UL-94 |
Class |
V.O |
| Limiting Oxygen Index (sheet 3mm thk) |
ASTM D 2863 |
% |
44 |
|